Kangbeite is transliterated from "compact laminate" in English. Kangbeite plate is made of decorative colored paper impregnated with melamine resin, multi-layer black or brown kraft paper impregnated with phenolic resin, and then pressed by steel plate under high temperature (150 ℃) and high pressure (1430psi). The thickness can be made from 1.6mm to 25mm. Blistering sometimes occurs during the use of anti magnification plate. How to find the cause of blistering and how to solve it.

首先，如果起泡處挑破后現(xiàn)牛皮紙底板，則說(shuō)明所購(gòu)買(mǎi)的抗倍特板有問(wèn)題，質(zhì)量不好。如果是起泡出挑破后現(xiàn)基材，則說(shuō)明施工不成熟，為施工不當(dāng)造成的原因。下面就來(lái)介紹下導(dǎo)致抗倍特板起泡的施工原因及避免方法。

First of all, if the kraft paper bottom plate is found after the blister is broken, it indicates that the purchased anti magnification plate has a problem and the quality is not good. If the base material appears after bubbling and breaking, it indicates that the construction is immature, which is caused by improper construction. The following is to introduce the construction causes and avoidance methods of anti double plate foaming.

抗倍特板起泡的施工原因：

Construction reasons for blistering of anti magnification plate:

施工時(shí)施壓不夠，不均勻

Insufficient and uneven pressure during construction

膠水局部未干就貼合；

The glue is not dry locally;

晾置時(shí)間不夠，不均勻

The drying time is not enough and uneven

濕氣重，出現(xiàn)假干現(xiàn)象

Heavy moisture and false dryness

板材潮濕，粘不牢；

The board is wet and cannot be adhered firmly;

膠水涂刷局部過(guò)多，干不了；

Too much glue can not be applied locally;

膠水局部缺膠。

Local glue shortage.

抗倍特板起泡的避免方法；

Methods to avoid blistering of anti doubling plate;

均勻用力施壓致防火板貼合。

Apply pressure evenly to make the fireproof board fit.

適當(dāng)延長(zhǎng)晾置時(shí)間

Properly extend the drying time

通風(fēng)干燥、用太陽(yáng)燈照射或跟換場(chǎng)所；

Ventilate and dry, shine with a sun lamp or change places;

粘物晾干或烘干后再使用；

The sticky material can be used after drying or drying;

均勻、一次刮膠。

Apply glue evenly and once.